您好! 欢迎您到访科晶智达官方网站                                                                                                                                                                                    本公司提供锂电池研发实验装备、锂电池生产中试线装备、锂电池安全检测设备,光电特种包装等全套解决方案。   欢迎订购 !                                                                                                                                                                                    感谢国内、港澳台地区及海外2000+ 高校、科研院所及企业对科晶智达长期以来的信赖与支持 !                                                                                                                                                                                    

NVP-20um 磷酸钒钠(NVP)钠离子电池正极材料

应用范围:高振实密度钠离子电池正极材料磷酸钒钠,具有比容量高、倍率性能优异及循环寿命长等优势。其对应于3.4 V(相对于金属Na电极)的电压平台和117.6 mAh/g的理论容量,主要应用于大规模储钠离子储能技术技术。

产品型号:NVP-20um

上架时间:2020-12-23

产品简述 产品详情 产品视频 留言咨询
       高振实密度钠离子电池正极材料磷酸钒钠,具有比容量高、倍率性能优异及循环寿命长等优势。其对应于3.4 V(相对于金属Na电极)的电压平台和117.6 mAh/g的理论容量,主要应用于大规模储钠离子储能技术技术。
  技术参数
化学式 Na3V2(PO4)3
应用 钠离子电池正极材料
标准包装 5克/瓶
生产厂家 湖北恩耐吉科技有限公司
1.X射线衍射分析 由XRD衍射分析结果可知,本产品为纯相钠超离子导体结构的磷酸钒钠,无其他杂志相产生。

1

2.扫描电镜结果 有SEM图像可知,产品为均匀球体,而EDS结果可知磷酸钒钠球体表面包覆均匀的无定形碳层。

1

3.充放电曲线图 由1C充放电曲线图可知,磷酸钒钠有一对充放电平台,其有V3+/V4+间的氧化还原反应造成。

1

4.循环寿命 有1C及10C循环寿命图可知,本公司生产磷酸钒钠具有优异的循环稳定性,1C充放电电流密度下,循环200圈后,容量无衰减。而在10C电流密度下,首次放电比容量高于105 mA h/g,循环2000圈后,放电容量依然高于85 mA h/g,容量保持率高于80%。

1       1

5.其他基本物理参数

1

       Na3V2(PO4)3, a cathode material of sodium-ion battery with high tap density, was developed by Hubei Energy Technology Co., LTD. This product possesses many advantages, such as high specific capacity, excellent rate performance and long cycle life. Moreover, the higher energy density with the potential of 3.4 V (vs Na metal) and the theoretical capacity of 117.6 mA h g-1 can be obtained. It is very suitable for being applied in large-scale energy storage.
1.X-ray diffraction analysis The XRD pattern shows that the product is the pure phase, Na3V2(PO4)3, and no impurity phase can be detected.

1

2.SEM SEM image shows that the product presents the uniform sphere morphology, and the result of EDS shows that the surface of Na3V2(PO4)3 are coated with uniform amorphous carbon layer.

1

3.The Charge-discharge curve According to the 1C charging-discharging curve, Na3V2(PO4)3 possesses a pair of charging-discharging platforms, which is caused by the redox reaction of V3+/V4+.

1

4.Cycle life From the cycle performance of Na3V2(PO4)3 at the current density of 1C and 10C, it can be found that our product presents the excellent cycle stability. Under the current density of 1C, the capacity has no evident degradation after 200 cycles. Moreover, under the current density of 10C, the initial specific discharge capacity of 105 mA h g-1, can be maintained about 80% after 2000 cycles.

1       1

5.Other physical parameters

1

暂无内容
暂无内容

留言咨询

* 产品型号:

不能为空

* 产品名称:

不能为空

* 访客姓名:

不能为空

* 访客手机:

手机号格式不对

* 访客 QQ:

必须是数字

* 电子邮箱:

E-mail格式不对

* 详细地址:

不能为空

* 留言内容:

不能为空

免责声明:本站产品介绍内容(包括产品图片、产品描述、技术参数等),仅供参考。可能由于更新不及时,或许导致所述内容与实际情况存在一定的差异,请与本公司客服人员联系确认。本站提供的信息不构成任何要约或承诺,科晶公司不定期完善和修改网站任何信息,恕不另行通知。

  • 哔哩哔哩

  • 抖音

  • 材料商城

  • 手机淘宝

  •  |  网站首页  |  关于我们  |  设备产品  |  光电包装  |  新闻资讯  |  解决方案  |  技术支持  |  人力资源  |  合作客户  |  视频中心  |  联系我们  | 

    Copyright @ 2011-2022 .深圳市科晶智达科技有限公司 Tel:0755-26959531 邮箱:info@szkejing.com

    粤ICP备11079497号

    在线
    客服

    售前咨询 09:00-17:30

    技术
    支持

    技术支持 09:00-17:30

    销售
    热线

    0755-26959531 5*8小时销售服务热线

    售后
    热线

    400-8865-130 售后服务热线

    关注
    微信

    关注官方微信

    小程序
    商城

    小程序商城

    付款
    信息

    微信付款

    支付宝付款

    在线
    留言

    请提交您的留言

    * 姓名:

    不能为空

    * 手机:

    手机号格式不对

    * 邮箱:

    E-mail格式不对

    * 内容:

    不能为空